The Effect of Alkali Soaking Time Variations (NaOH) on the Strength of Pinapple Fiber Composite (Ananas Cosmosus)
Pengaruh Variasi Waktu Perendaman Alkali (NaOH) terhadap Kekuatan Komposit Serat Nanas (Ananas Cosmosus)
DOI:
https://doi.org/10.21070/ups.7289Keywords:
Alkaline TreatmentAbstract
Pineapple leaves contain high levels of fiber and can be used as a composite reinforcing material. The aim of this research was to determine the effect of 5% alkali treatment with variations of 2, 4, 8, 16 and 24 hours of immersion on the mechanical properties of composites reinforced with pineapple leaf fiber using a volume fraction of 30% with straight fiber orientation. For tensile test specimens refer to ASTM D638 and ASTM D790 bending tests. Results of the tensile test on the effect of alkaline immersion showed that the largest stress was 44.82 N/mm² in 24 hour immersion, the largest strain was 0.1080% in 24 hour treatment and the largest modulus of elasticity was 422.41 N/mm² in 8 hour treatment. Meanwhile, the results of the bending test showed that the largest bending stress was 122 N/mm² in 16 hours of treatment and the largest modulus elasticity was 14616 N/mm².
Downloads
References
E. Putra, D. Boangmanalu, A. Qadry, F. Taruyun, H. Sinaga, and A. B. Pratama, “uji kekuatan tarik komposit penguat serat sabut kelapa,” vol. 05, no. 01, pp. 56–63, 2024.
Nurfajri and K. Arwizet, “Analisis Kekuatan Tarik Komposit Serabut Kelapa Dan Ijuk Dengan Perlakuan Alkali (NaOH),” J. Multidicsiplinary Res. Dev., vol. 1, no. 4, pp. 791–797, 2019, [Online]. Available: https://jurnal.ranahresearch.com/index.php/R2J/article/view/130
M. Syahrul Ramadhan and L. Rislya Prakasa, “Analisis Kekuatan Tarik Material Komposit Serat Alam Daun Agel Dengan Variasi Matrik Epoxy Dan Polyester,” J. Penelit., vol. 6, no. 3, pp. 194–203, 2021, doi: 10.46491/jp.v6i3.567.
S. Supriyanto, “Karakterisik Kekuatan Komposit Serat Daun Nanas Dengan Variasi Panjang Serat,” J. Mesin Nusant., vol. 4, no. 1, pp. 30–39, 2021, doi: 10.29407/jmn.v4i1.16039.
M. T. Marantika, I. Sujana, and M. Ivanto, “Analisa uji tarik komposit berpenguat serat daun nanas dengan variasi susunan menggunakan perlakuan alkali,” J. Teknol. Rekayasa Tek. Mesin, vol. 3, no. 1, pp. 62–68, 2022.
L. Widodo, K. Priyanto, and B. Margono, “Analisis Ketangguhan Impak Komposit Polyester Berpenguat Serat Daun Nanas Berdasarkan Jenis Anyaman,” Teknika, vol. 7, no. 4, pp. 217–227, 2022, doi: 10.52561/teknika.v7i4.207.
D. K. Sari and M. I. Sari, “Karakteristik Karbon Aktif Dari Limbah Daun Nanas (Ananas comosus)Dengan Aktivator H3PO4 1 M,” J. Tek. Patra Akad., vol. 12, no. 01, pp. 51–56, 2021, doi: 10.52506/jtpa.v12i01.127.
A. Nasir, et, “Efek Perlakuan Alkali Natrium Hidrosikda Terhadap Karakter Fisis dan Mekanis Komposit Serat Nanas Dengan Penguat Resin Poliester,” vol. 9, pp. 356–363, 2023.
F. Husaini, S. M. B. Respati, and M. Dzulfikar, “Pengaruh Variasi Fraksi Volume Dan Arah Serat Pada Komposit Matrik Resin Polyester Berpenguat Serat Pelepat Lontar (Borassus Flabellifer) Dengan Perlakuan NaOH 5% Terhadap Kekuatan Uji Tarik,” J. Ilm. Momentum, vol. 16, no. 1, 2020, doi: 10.36499/mim.v16i1.3349.
E. Widodo and I. Dwiyoga, “Analisis Pengaruh Alkalisasi NaOH Terhadap Serat Daun Nanas Sebagai Penguat Bio Komposit,” Otopro, vol. 18, no. 1, pp. 1–6, 2022, doi: 10.26740/otopro.v18n1.p1-6.
A. M. F. H, Tjahjanti P, “Study of Crack Connections in Materials Composite Based on Polymer Study of Crack Connections in Materials Composite Based on Polymer,” 2020, doi: 10.1088/1757-899X/874/1/012026.
S. H. Nuri, T. Suwanda, and K. Diharjo, “Kajian Komprehensif Pengaruh Alkali Terhadap Kekuatan Komposit Berpenguat Serat Nanas-Nanasan (Bromeliaceae),” J. Ilm. Semesta Tek., vol. 9, no. 2, pp. 199–207, 2006.
M. B. N. Rahman, T. Suwanda, and K. Diharjo, “Studi Optimasi Peningkatan Kekuatan Bending Komposit Berpenguat Serat Nanas-Nanasan (Bromeliaceae) Kontinu Searah,” J. Ilm. Semesta Tek., vol. 11, no. 2, pp. 207–217, 2008.
K. Diharjo, “Pengaruh Perlakuan Alkali terhadap Sifat Tarik Bahan Komposit,” J. Tek. Mesin, 2008.
W. Rachmadi and T. H. Ningsih, “Optimasi Perlakuan Konsentrasi Dan Waktu Perendaman NaOH Serta Fraksi Volume Pada Komposit Serat Kulit Jagung Terhadap Pengujian Bending Metode Taguchi,” Jinggo, vol. 2, no. 1, pp. 30–38, 2023, [Online]. Available: http:https://jurnal.poliwangi.ac.id/index.php/jinggo/
Syahrinal Anggi Daulay, Fachry Wirathama, and Halimatuddahliana, “Pengaruh Ukuran Partikel Dan Komposisi Terhadap Sifat Kekuatan Bentur Komposit Epoksi Berpengisi Serat Daun Nanas,” J. Tek. Kim. USU, vol. 3, no. 3, pp. 13–17, 2014, doi: 10.32734/jtk.v3i3.1628.
I. Shah, L. Jing, Z. M. Fei, Y. S. Yuan, M. U. Farooq, and N. Kanjana, “A Review on Chemical Modification by using Sodium Hydroxide (NaOH) to Investigate the Mechanical Properties of Sisal, Coir and Hemp Fiber Reinforced Concrete Composites,” J. Nat. Fibers, vol. 19, no. 13, pp. 5133–5151, 2022, doi: 10.1080/15440478.2021.1875359.
S. D. Babatunde, “Synthesis and Characterisation of Sugarcane Bagasse and Pineapple Leaf Particulate Reinforced Polyester Resin Matrix Composites,” vol. 35, no. 3, pp. 1091–1100, 2022, doi: 10.35378/gujs.787964.
A. Alamsyah, T. Hidayat, and A. N. Iskandar, “Pengaruh Perbandingan Resin Dan Katalis Terhadap Kekuatan Tarik Komposit Fiberglass-Polyester Untuk Bahan Pembuatan Kapal,” Zo. Laut J. Inov. Sains Dan Teknol. Kelaut., vol. 2, no. 2, pp. 26–32, 2020, doi: 10.62012/zl.v1i2.10760.
E. F. Samsara, Pengaruh Variasi Infill Pattern Terhadap Kuat Tarik dan Kuat Bending Filamen Polylactid Acid Pada Hasil Cetak Mesin Ender-3 Pro, no. 0. 2016.
R. Lumintang, F. A. Rauf, and G. D. Soplanit, “Ketahanan Bending Komposit Matriks Poliester Berpenguat Serat Sabut Kelapa,” J. Tekno Mesin, vol. 5, no. 2, pp. 88–94, 2019.
J. T. Mesin, S. Pengajar, and U. M. Sidoarjo, “Pengaruh Model Speciment Uji Tarik Pada Pengelasan Besi Fc-30 Di Lihat Dari Kekuatan Tarik Pengelasan,” vol. 1, no. 2, pp. 29–36, 2016.
Gugun Gundara, Agung Setia Nurzein, Acep Wagiman, and Asep Romi Ramadhan, “Effect of Alkalized Pineapple Leaf Fiber Direction Variations on Tensile Strength and Bending of Polyester Matrix Composites,” Formosa J. Sustain. Res., vol. 2, no. 1, pp. 87–96, 2023, doi: 10.55927/fjsr.v2i1.2703.
A. Kadir, A. Aminur, and M. Aminur, “Pengaruh Pola Anyaman Terhadap Kekuatan Tarik Dan Bending Komposit Berpenguat Serat Bambu,” Din. J. Ilm. Tek. Mesin, vol. 6, no. 1, pp. 9–18, 2015, doi: 10.33772/djitm.v6i1.262.
N. H. Sari and S. Sinarep, “Analisa Kekuatan Bending Komposit Epoxy Dengan Penguatan Serat Nilon,” Din. Tek. Mesin, vol. 1, no. 1, 2011, doi: 10.29303/d.v1i1.130.
R. Kartini, D. H, and Sudirman, “Polimer Berpenguat Serat Alam,” J. SainsMateri Indones., vol. 3, no. 3, pp. 30–38, 2002.
A. E. Purkuncoro, “Pengaruh Perlakuan Alkali (Naoh) Serat Ijuk (Arenga Pinata) Terhadap Kekuatan Tarik,” J. Tek. Mesin Transm., vol. 13, no. 2, pp. 167–178, 2017.
A. Nurdin, S. Hastuti, H. P. D., and R. H., “Pengaruh Alkali dan Fraksi Volume terhadap Sifat Mekanik Komposit Serat Akar Wangi – Epoxy,” Rotasi, vol. 21, no. 1, p. 30, 2019, doi: 10.14710/rotasi.21.1.30-35.
B. Maryanti, A. A. Sonief, and S. Wahyudi, “Pengaruh Alkalisasi Komposit Serat Kelapa-Poliester Terhadap Kekuatan Tarik,” Rekayasa Mesin, vol. 2, no. 2, pp. 123–129, 2011.
J. J. S. Nesimnasi, K. Boimau, and Y. M. Pell, “Pengaruh Perlakuan Alkali (NaOh) pada Serat Agave Cantula terhadap Kekuatan Tarik Komposit Polyester,” J. Tek. Mesin, vol. 2, no. 1, pp. 29–38, 2015, [Online]. Available: http://ejournal-fst-unc.com/index.php/LJTMU
W. A. Prasetyo, D. M. Gunara, and J. T. Penerbangan, “Analisis Perbandingan Kekuatan Tarik Orientasi Unidirectional 0° Dan 90° Pada Struktur Komposit Serat Mendong Dengan Menggunakan Epoksi Bakelite Epr 174,” Infomatek, vol. 19, no. 02, pp. 57–64, 2017.
H. Hestiawan and A. Fauzi, “Studi Pengaruh Fraksi Volume dan Susunan Serat Terhadap Kekuatan Tarik dan Bending Komposit Resin Berpenguat Serat Rotan ( Calamus Trachycoleus ),” J. Mech., vol. 5, no. 1, pp. 3–6, 2014.
J. L. Marpaung, A. Sutrisno, and R. Lumintang, “Penerapan Metode Anova Untuk Analisis Sifat Mekanik Komposit Serabut Kelapa,” J. Online Poros Tek. Mesin, vol. 6, no. 2, pp. 151–162, 2017.
N. P. G. Suardana and N. M. Dwidiani, “Pengaruh Waktu Treatment Serat terhadap Sifat Mekanik Komposit Serat Tapis Kelapa,” J. Tek. Ind., vol. 8, no. 2, pp. 188–192, 2008, doi: 10.22219/jtiumm.vol8.no2.188-192.
Downloads
Additional Files
Posted
License
Copyright (c) 2025 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.