Analysis of the Effect of Current Variation on GTAW Welding Reviewed from Tensile Testing on ASTM A36 Plate Material
Analisa Pengaruh Variasi Arus pada Pengelasan GTAW di Tinjau dari Pengujian Tarik pada Material Plat ASTM A36
DOI:
https://doi.org/10.21070/ups.662Keywords:
ASTM A36, Tensile Test, Gas Tungsten Arc WeldingAbstract
This research was conducted by varying the amperage current to determine the weld strength of the ASTM A36 steel plate material during the tensile test. From the results of the tensile test, the highest tensile value was obtained with welding parameters 130A, gas flowrate 5-10, single V connection type with an angle of 60° on specimen 2 with a tensile value of 46.58 Kgf/mm2. At a current strength of 160A, the highest tensile value was obtained on specimen 3 with a tensile value of 45.64 Kgf/mm2 using a gas flow rate of 5-10, a single V type connection with an angle of 60°. While the 190A current strength obtained the highest tensile value in specimen 1 with a tensile value of 54.37 Kgf/mm2 using a gas flowrate of 5-10, a single V connection type with an angle of 60°.
Downloads
References
O. W. Blodgett, Structural Welding Code-Steel, Florida: American Welding Society, 2001.
A. Setiawan and Y. A. Y. Wardana, "Analisa Ketangguhan dan Struktur Mikro pada Daerah Las dan HAZ Hasil Pengelasan Sumerged Arc Welding pada Baja SM 490," JURNAL TEKNIK MESIN, vol. 8, no. 2, pp. 57-63, 2006.
A. Rahmatika, S. Ibrahim , M. Hersaputri and E. Aprilia, "Studi Pengaruh Variasi Kuat Arus Terhadap Sifat Mekanik Hasil PEngelasan GTAW Alumunium 1050 dengan Filler ER 4043," J. Polimesin, vol. 17, no. 1, pp. 47-54, 2019.
S. Widharto, Petunjuk Kerja Las, Jakarta: Penebar Swadnya, 2006.
A. Marwanto, Shield Metal Arc Welding, Yogyakarta: Universitas Negeri Yogyakarta, 2007.
D. Teknik Las GTAW, Jakarta: Direktorat Jendral Peningkatan Mutu Pendidik dan Tenaga Kepenidikan, 2013.
S. Arifin, Las Listrik dan Otogen, Jakarta: Ghalia Indonesia, 1997.
D. Ratnasari, Pengaruh Voltage pada Gas Metal Arc Welding (SMAW) terhadap Struktur Mikro dan Tegangan Lentur (Face and Root) EMS 45 dengan Sambungan Kapuh V, Semarang: Universitas Negeri Semarang, 2016.
H. Wiryosumarto, Teknik Pengelasan Logam. Cetakan ke-7, Jakarta: PT. Pradya Paramitha, 1996.
T. Surdia and S. Saito, Pengetahuan Bahan Teknik, Jakarta: Pradnya Paramita, 2006.
R. Dani, Pengaruh Variasi Kecepatan Pengelasan Tungsten Inert Gas (TIG) Terhadap Kekuatan Tarik Hasil Sambungan Las Pada Baja Karbon Rendah (ST 41), Lampung: Universitas Lampung, 2016.
Siswanto, Konsep Dasar Teknik Las (Teori dan Praktik), Jakarta: PT. Prestasi Pustakarya, 2011.
D. Perdana, Analisa Pengaruh Variasi Arus Pengelasan GTAW pada Material Plat SS 400 Disambung dengan Material Plat SUS 304 Terhadap Sifat Mekanis, Sidoarjo: Universitas Maarif Hasyim Latif, 2016.
G. A. Bintoro, Dasar-dasar Pekerjaan Las, Yogyaarta: Kanisius, 2000.
H. Wiryosumarto and O. Toshie, Teknologi Pengelasan Logam. Cetakan Ke-8, Jakarta: PT Pradnya Paramita, 2000.
Downloads
Additional Files
Posted
Categories
License
Copyright (c) 2023 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.