The Influence of SMAW Welding Process Parameters on Hardness and Microstructure of AISI 1050 Steel
Pengaruh Parameter Proses Pengelasan SMAW Terhadap Kekerasan Dan Struktur Mikro Pada Material AISI 1050
DOI:
https://doi.org/10.21070/ups.5787Keywords:
SMAW welding, AISI 1050 steel, Brinell hardness, Microstructure, Welding process parameters, Welding current, Cooling method, CappingAbstract
This study evaluates the impact of SMAW welding process parameters on AISI 1050 steel, focusing on variations in welding current, cooling method, and capping on weld hardness and microstructure. Brinell hardness test results indicate that the cooling method has the greatest influence (55.02%) on hardness variation, followed by welding current (24.57%) and capping (9.57%). The optimal parameters are 2 capping with 100A current and air cooling, which result in the highest hardness (222 HRB), while the lowest hardness is observed with 2 capping, 80A current, and oil cooling (190 HRB). Microstructural analysis shows that the combination of 2 capping with 80A current and oil cooling yields a balanced microstructure with minimal defects, whereas 120A current and air cooling cause microstructural instability and increased defects. This study highlights the importance of controlling process parameters for achieving high-quality welds.
Downloads
References
Purba Z, Bahri S, Syarif Jurusan Teknik Mesin Politeknik Negeri Lhokseumawe Jlbanda Aceh-Medan Km J. Pengaruh Variasi Kampuh Las Terhadap Ketangguhan Sambungan Hasil Pengelasan Material Baja AISI 1050 The Effect Of Weld Groove Variations On The Toughness Of Welding Joints Of AISI 1050 Material. J Weld Technol. 2022;4(1):27–33.
Islamuddin N, Soedarmaji W. Analisa Uji Tekan, Kerapatan Densitas Dan Mikrostruktur Terhadap Komposit Bahan Baku Teakwood Serbuk Gergaji Kayu Nurkholis Islamuddin 1) , Wisma Soedarmadji 2) Fakultas Teknik, Program Studi Teknik Mesin Universitas Yudharta Pasuruan. J Mech Manuf Technol. 2020;1(2):58–65.
Santoso TB, Solichin, Hutomo PT. Pengaruh Kuat Arus Listrik Pengelasan Terhadap Kekuatan Tarik Dan Struktur Mikro Las SMAW Dengan Elektroda E7016. J Rekayasa Mesin. 2020;15(1):20.
Teknik J, Politeknik M, Lhokseumawe N. Analisa Pengaruh Proses GTAW Dan SMAW Terhadap Ketangguhan Sambungan Pengelasan Material AISI 1050. (1):19–25.
Chairul N, Irzal I, Mulianti M, Nurdin H. Pengaruh Variasi Kuat Arus Terhadap Kekuatan Tarik Hasil Pengelasan Smaw Pada Baja Karbon Rendah Dengan Elektroda E-7018. J Vokasi Mek. 2022;4(4):167–72.
Pandapotan U, Mulyadi M. Pengaruh Media Pendingin Terhadap Porositas Dan Kekuatan Tarik Menggunakan Pengelasan SMAW DCSP Pada Material Pipa Baja Karbon SCH40. Innov Technol Methodical Res J. 2024;3(3):8.
Mauliza A, Usman S. Analisa Pengaruh Arus Terhadap Kekuatan Tarik Material Baja Karbon AISI 1050 Hasil Pengelasan SMAW. J Weld Technol Vol [Internet]. 2022;4(1):22–6. Available From: Https://Media.Neliti.Com/Media/Publications/436420-Analysis-Of-The-Effect-Of-Current-On-Ten-E4d77915.Pdf
Hamid A. Analisa Pengaruh Arus Pengelasan Smaw Pada Material Baja Karbon Rendah Terhadap Kekuatan Material Hasil Sambungan. J Teknol Elektro. 2016;7(1):26–36.
Azwinur, Saputra Ismy A, Nanda R, Ferdiyansyah. Pengaruh Arus Pengelasan SMAW Terhadap Kekuatan Sambungan Las Double Lap Joint Pada Material AISI 1050. J Weld Technol. 2020;2(1):1–7.
Ainur Rosidah A, Suheni S, Wisnu Anarki E. Analisis Pengaruh Diameter Elektroda Dan Kecepatan Las Terhadap Sifat Mekanik Dan Struktur Makro Pada Baja AISI 1050 Dengan Proses Pengelasan TIG. Pros SENASTITAN Semin Nas Teknol Ind Berkelanjutan [Internet]. 2021;1(1):414. Available From: Https://Ejournal.Itats.Ac.Id/Senastitan/Article/View/1669
Metode M, Smaw LAS, Tig DAN. Edisi Cetak Jurnal Dinamis , Juni 2020 ( ISSN : 0216-7492 ). 2020;(1):1–7.
Purwanto A, Wijoyo W, Fajar Riyadin A. Pengaruh Polaritas Mesin Las Pada Pengelasan SMAW (Shielded Metal Arc Welding) Terhadap Sifat Fisik Dan Mekanik Baja Karbon Rendah. J Tek Indones. 2023;2(4):150–8.
Anwar S, Mulyadi M. Pengaruh Media Pendingin Terhadap Kekerasan Dan Struktur Mikro Hasil Pengelasan SMAW Pegas Daun Mitsubishi PS 120. Innov Technol Methodical Res J. 2024;3(2):1–11.
Syahrillah Gusti RF, Firman M, Sugeng .P MA. Analisa Uji Kekerasan pada Poros Baja ST 60 dengan Media Pendingin yang Berbeda. Al-Jazari J Ilm Tek Mesin. 2016;01(02):21–6.
Downloads
Additional Files
Posted
License
Copyright (c) 2024 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.