Effect of Current and Electrode in Welding ASTM A36 Material on Tensile Strength
Pengaruh Arus dan Elektroda Pada Pengelasan Material ASTM A36 Terhadap Kekuatan Tarik
DOI:
https://doi.org/10.21070/ups.4470Keywords:
Electrode, current strength, ASTM A36, SMAW, Tengsile TestAbstract
Welding is a very common process found in the industrial and construction worlds. The objective of this research is to determine the effect of electrode type and current strength on the tensile strength of ASTM A36 steel plates. The process parameters in this study involve variations in electrode type and current strength. The electrodes used are NK 68, RB 26, and RD 460, while the current strengths used are 80, 90, and 100 Amperes. it is found that the tensile testing of the welded joints using NK 68, RB 26, and RD 460 electrodes showed that the RD 460 electrode has a greater tensile strength compared to NK 68 and RB 26 electrodes. The highest tensile strength of the RD 460 electrode is at a current of 90 amperes. At 90 Amperes, these conditions are closer to ideal conditions, which contributes to higher draw values.
Downloads
References
D. Irawan, R. P. Wardhani, P. Studi, T. Mesin, F. Teknik, and U. Tridharma, “Analisis Perbandingan Kekuatan Tarik Hasil,” vol. 3, no. 1, pp. 1–13, 2020.
M. W. Ilham, “Analysis of Electrodes Combination in Stainless Steel and Welded Steel ,” 2017.
P. Studi, T. Perkapalan, F. Teknik, and U. Diponegoro, “Analisis Kekuatan Sambungan Las Smaw ( Shielded Metal Arc Welding ) Pada Marine Plate St 42 Akibat Faktor Cacat Porositas Dan Incomplete Penetration,” Kapal, vol. 5, no. 2, pp. 102-113–113, 2012, doi: 10.12777/kpl.5.2.102-113.
I. D. Kurniati et al., Buku Ajar. 2015.
K. Tarik, D. A. N. Struktur, P. Baja, A. Dengan, and P. Smaw, PENGARUH SUDUT SINGLE V JOINT TERHADAP LAJU ELEKTRODA PADA KOROSI , KEKUATAN TARIK DAN STRUKTUR MIKRO PELAT BAJA A36 DENGAN PENGELASAN SMAW. 2023.
Miftahul Huda ST. MPD and F. Setiawan, “V Dan Kuat Arus Dengan Las ( Smaw ) Pada Baja a36 Terhadap,” pp. 1–9, 2016.
J. Arifin, H. Purwanto, and I. Syafa’at, “Pengaruh Jenis Elektroda Terhadap Sifat Mekanik Hasil Pengelasan,” Momentum, vol. 13, no. 1, pp. 27–31, 2017.
A. Suprayogi and P. H. Tjahjanti, “Analisa Surface Preparation Pada Plat Baja ASTM A36,” Res. Rep., pp. 188–197, 2017.
M. Mulyadi, “Pengaruh Model Speciment Uji Tarik Pada Pengelasan Besi Fc-30 Di Lihat Dari Kekuatan Tarik Pengelasan,” Rekayasa Energi Manufaktur, vol. 1, no. 2, p. 29, 2016, doi: 10.21070/r.e.m.v1i2.658.
D. W. H. Kusumaning Gutama, “Pengaruh Arus Pengelasan Dan Jenis Elektroda Terhadap Kekuatan Tarik Pada Steel 42,” J. Tek. Mesin, vol. 1, no. 3, pp. 43–47, 2013.
dan S. Wahyudi, R., Nurdin., “Analisa Pengaruh Jenis Elektroda Pada Pengelasan SMAW Penyambungan Baja Karbon Rendah Dengan Baja Karbon Sedang Terhadap TYensile Strenght,” J. Weld. Technol., vol. 1, no. 2, pp. 43–47, 2019.
F. Ryan Afrianzah and Frizka Vietanti, “Analisa Pengaruh Variasi Arus dan Jenis Elektroda Pengelasan SMAW terhadap Cacat Las dan Kekerasan Material Baja A36,” no. Senastitan Iii, pp. 1–5, 2023.
K. Tarik, D. Struktur, B. Surono, T. C. Wahyudi, E. Nugroho, and S. Santoso, “Pengaruh Jenis Elektroda Pada Sambungan Las Plat Baja Terhadap,” vol. 12, no. 02, pp. 363–371, 2023.
R. D. M. Ridzkiansyah and Y. Irwan, “Analisa Pengaruh Jenis Elektroda Pengelasan SMAW Pada Penyambungan Baja ASTM A36 Dengan Baja Tahan Karat AISI 304 Terhadap Sifat Mekanis,” pp. 1–6, 2021.
“No Title,” 2022.
M. Dikwan, S. Jokosisworo, and A. F. Zakki, “Pengaruh Normalizing Terhadap Kekuatan Tarik , Impak dan Mikrografi Pada Sambungan Las Baja A36 Akibat Pengelasan SMAW Dengan Variasi 2 Waktu Pemanasan,” Tek. Perkapalan, vol. 5, no. 2, pp. 421–430, 2017.
Downloads
Additional Files
Posted
License
Copyright (c) 2024 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.