The Influence of Welding Technique with Variation of Current on Surface Defects and Penetration of ST40 Steel
Pengaruh Teknik Pengelasan dengan Variasi Arus Terhadap Cacat Permukaan dan Penetrasi pada Baja ST40
DOI:
https://doi.org/10.21070/ups.3837Keywords:
Welding Technique, Current Variation,, Macro Test,, Non Destructive testAbstract
one of the conection of one place starting from several materials or materials that are solid is one of the welding methods, as for the factors that can affect the quality of the weld result wich include the process of tools and materials to e used, welding direction, welding electrode movement patterns, in order to use and select electrodes, In this study ST 40 steel plate, testing was carried out with 3 specimens using U ang zig-zag movement patterns and the direction of welding used ack and forth. Variations in electric current used 40 A, 60 A, 80 A. This study has the aim of influencing welding tehniques using current variatoins. The test results that the welding process using welding tehniques consisting of movement patterns, welding direction ang welding time does not affect the weld defects in the welding results. Welds defects that occur due to variations in the current used.
Downloads
References
V. D. Primazda dan N. Y. Nugroho, “Sifat Mekanik Pengelasan Smaw Pada Baja Astm A36 Terhadap Variasi Preheating,” in Implementasi Hasil Riset Sumber Daya Laut dan Pesisir Dalam Peningkatan Daya Saing Indonesia, 2019, hal. 54–60.
A. N. Akhmadi dan M. T. Qurrohman, “analisa hasil pengelasan 2G dan 3G dengan bahan plat besi ST 40 ketebalan 10 MM dan Voltase 20-35 menggunakan mesin las MIG,” Nozzle J. Mech. Eng., vol. 9, no. 2, hal. 25–30, 2020.
A. Saputra, “Pengaruh Amper Terhadap Cacat Las Pada Pengelasan Baja Lunak Dengan Menggunakan Pengelasan Smaw Posisi Pengelasan 2F,” 2021.
A. Marwanto, Shield Metal Arc Welding. Yogyakarta, 2007.
Y. Miranda dan A. M. Made, “Analisa Perbedaan Temperatur Pada Material Baja Karbon Rendah S355JO Terhadap Distorsi Pada Pengelasan SMAW,” Zo. Mesin, vol. 9, no. 1, hal. 10–18, 2018.
Y. Bontong, “Analisis Pengaruh Arus Pengelasan Dengan Metode SMAW Dengan Elektroda E7018 Terhadap Kekuatan Tarik Dan Ketangguhan Pada Baja Karbon Rendah,” hal. 1–18.
I. Saefuloh, I. Setiawan, H. Istiqlaliyah, Wijoyo, dan A. B. Ulum, “Analisa pengaruh pola gerak elektroda dan kuat arus terhadap kekuatan tarik, kekerasan, dan struktur mikro baja SS400,” Tek. J. Sains dan Teknol., vol. 15, no. 09, hal. 143–148, 2019.
F. M. Rusdi dan H. Istiqlaliyah, “Study Of The Effect Of Welding Current Variations On Joint Strength And Microstructure Of Cracker Lontongan Chopper Machine,” SINTEK J., vol. 17, no. 2, hal. 120–129, 2023.
A. Asni B, M. Waruni K, dan M. Jaya M, “Identifikasi Citra Cacat Las Menggunakan MetodeGray Level Co-Occurance Matrix (GLCM) dan K-NN,” JTE UNIBA, vol. 7, no. 1, hal. 261–268, 2022.
F. Pambudi, H. Athallah, H. Abizar, dan A. Yhuto W.P, “Analisis Pengujian Non Destructive Test Terhadap Hasil Cacat Las SMAW Menggunakan Metode Visual Test,” Semin. Nas. KEPENDIDIKAN FKIP UST, vol. 1, no. 1, hal. 23–32, 2022.
S. A. M. I. Naufal, U. Budiarto, dan S. J. Sisworo, “Pengaruh Variasi Arus Las SMAW Terhadap Laju Korosi dan Kekuatan Tarik Baja ST 40,” J. Tek. Perkapalan, vol. 09, no. 2, hal. 191–198, 2021.
B. Bagaskara, S. M. B. Respati, dan M. Dzulfikar, “Pengaruh Posisi Pengelasan Terhadap Kekuatan Tarik, Foto Makro Dan Mikro Pada Baja ST 37 Dengan Pengelasan Smaw Untuk Rangka Billboard,” Momentum, vol. 15, no. 2, hal. 132–136, 2019.
Erika dan N. H. Falahi, “Analisa Pengaruh Kuat Arus Las SMAW Terhadap Cacat Pengelasan,” PRESISI, vol. 24, no. 1, hal. 51–55, 2022.
Irwansyah, “Deteksi Cacat Pada Material Dengan Teknikpengujian Tidak Merusak,” LENSA, vol. 2, no. 48, hal. 7–14, 2019.
A. Fazadima, H. Pratikno, dan H. Ikhwani, “Analisis Pengaruh Variasi Heat Input terhadap Uji Impact, Uji Metalografi, dan Laju Korosi pada Pengelasan SMAW Sambungan Pelat Baja A36 dengan Baja Structural
Page | 7
Steel 400 (SS400),” J. Tek. ITS, vol. 11, no. 3, hal. 38–43, 2022.
A. E. Purkuncoro, “Analisis Pengaruh Variasi Arus Listrik 90 A,10 A, 130 A Terhadap Sifat Mekanis Dan Struktur Mikro Hasil Pengelasan Gas Metal Arc Welding (GMAW) Pada Baja Karbon JISS50C,” Ind. Inov. J. Tek. Ind., hal. 1–8, 2019.
Y. D. Anda, “Analisa Hasil Sambungan Las SMAW Pada Material Baja ASTM A36 Dengan Variasi Arus Dan Jarak Kampuh Las,” 2021.
A. A. Santoso, R. J. Pribadi, dan S. Raharja, “Deteksi Cacat Hasil Pengelasan Pada Baja Karbon Rendah Menggunakan Fungsi Transfer Untuk Non Destructive Test (NDT),” Pros. Semin. Nas. UNIMUS, vol. 5, hal. 105–115, 2022.
B. Sulistiyo, H. Purwanto, dan I. Syafa’at, “Analisis Pengaruh Arus Pengelasan GMAW Terhadap Struktur Makro, Mikro Dan Sifat Mekanik Pada Material Baja Karbon ASTM A36,” Momentum, vol. 17, no. 1, hal. 36–42, 2021.
A. Bahkhori, “Analisa Cacat Hasil Pengelasan Pada Baja Kabon Rendahterhadap Pengaruh Masukan Panas Las,” SEMNASTEK, hal. 90–95, 2021.
R. W. Sikumbang, M. K. Fahri, dan H. Abizar, “Pengaruh arus listrik terhadap hasil cacat las pada pengelasan SMAW,” Vocat. Educ. Natl. Semin., vol. 01, no. 01, hal. 66–70, 2022.
A. Ferdi Arfiansyah dan A. H. Ainur Rasyid, “Analisis Pengaruh Variasi Arus Pada Pengelasan SMAW Baja ST 60 Terhadap Kekuatan Tarik Dan Porositas,” JTM, vol. 11, no. 03, hal. 53–58, 2023.
G. Avilla, B. Suhendra, dan V. Naubnome, “Analisis Variasi Kuat Arus Dan Kelembapan Elektroda Pada Pengelasan SMAW Terhadap Cacat Las Pada Pengelasan Baja SS400 Dengan Metode Nondestructive Test (NDT) Penetrant Testing,” J. Kaji. Tek. mesin, vol. 8, no. 2, hal. 1–9, 2023.
Downloads
Additional Files
Posted
License
Copyright (c) 2024 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.