Cooling Effect Of Oxy Acetelyn Process Of Galvanized Plate Material On Corrosion
Pengaruh Pendinginan Pada Proses Oxy Acyteline Material Plat Terhadap Korosi
DOI:
https://doi.org/10.21070/ups.3185Keywords:
Cooling, Oxy Acetelyn, Plate Galvanized, CorrosionAbstract
Oxy acetelyn welding is a metal-to-metal joining process (welding) that uses acetelyn (C2H2) welding as fuel.The media used for cooling this time are air, water and oil. The purpose of this research is to find out wheteher there is corrosion on the galvanized plate if the cooling method used these 3 media with one plate and one media. The test was carried out using agalvanized plate with each media soaked for a few minutes then allowed to cool and then soaked using HCL. Then it can be calculated using the corrosion resistance formula and can be concluded with the results of air = 0,0006 mm/yy, Water CR = 0,0001 mm/yy, Oil CR = 0,0001 mm/yy or that galvanized plate material experience corrosion resistence by 3 types of the method
Downloads
References
M. Naufal, “PENGARUH NYALA API PADA LAS OXY-ACETYLENE TERHADAP KEKUATAN IMPAK PADA PROSES BRAZING BAJA KARBON RENDAH EFFECT OF FLAME ON OXY-ACETYLENE WELDING ON IMPACT STRENGHT OF LOW CARBON STEEL BRAZING PROCESS PROYEK AKHIR Laporan akhir ini dibuat dan diajukan untuk memenuhi salah satu syarat kelulusan Sarjana Terapan Diploma IV Politeknik Manufaktur Negeri Bangka Belitung Disusun Oleh,” 2020.
Azwar Said.)dan Siti Nurul Aida, “PENELITIAN BIOLIMNOLOGI SUMBER DAYA PERAIRAN BARU BEKAS TAMBANG TIMAH DI PULAU BANGKA DAN BELITUNG UNTUK BUDI DAYA IKAN,” 2018.
Cosmas Haryawan, “PEMANFAATAN SPARQL INFERENCING NOTATION (SPIN) DALAM PROTOTIPE PENCARIAN DATA RESTORAN BERBASIS SEMANTIK,” 2019.
A. H. Riandini, M. Sagaf, and A. Syakhroni, “PENERAPAN MANAJEMEN RISIKO KESELAMATAN DAN KESEHATAN KERJA DENGAN METODE HIRADC PADA PLTGU TAMBAK LOROK SEMARANG IMPLEMENTATION OF RISK MANAGEMENT OCCUPATIONAL HEALTH AND SAFETY WITH HIRADC METHOD AT PLTGU TAMBAK LOROK SEMARANG,” vol. 14, no. 1, pp. 11–18, 2023, doi: 10.34001/jdpt.
Mashadi Said, “KETIDAKLAZIMAN KOLOKASI PEMBELAJAR BIPA DAN IMPLIKASINYA TERHADAP PEMBELAJARAN BAHASA,” 2020.
H. Bisri, “PENGARUH MEDIA PENDINGINAN PADA PROSES PENGELASAN SMAW MATERIAL BAJA SS400 TERHADAP KEKUATAN TARIK DAN STRUKTUR MIKRO,” 2022.
S. & B. Harjanto. Ayub Budhi Anggoro, “KUALITAS REPAIR WELDING DENGAN METODE OKSI-ASETILIN DAN PERLAKUAN PREHEATING PADA CAST WHEEL ALUMUNIUM SEBAGAI SUPLEMEN MATERI MATA KULIAH TEKNIK PENGELASAN,” 2019.
Bambang Avip Priatna Martadiputra, “MODIFIKASI MEAs DENGAN MENGGUNAKAN DIDACTICAL DESIGN RESEARCH UNTUK MENINGKATKAN KEMAMPUAN BERPIKIR STATISTIS MAHASISWA,” 2021.
M. A. F. , H. A. , M. S. Rita Maria Veranika9, “STUDI PENGARUH VARIASI ELEKTRODA E 6013 DAN E 7018 TERDAHAP KEKUATAN TARIK DAN KEKERASAN PADA BAHAN BAJA KARBON RENDAH,” 2019.
M. Naufal, “PENGARUH NYALA API PADA LAS OXY-ACETYLENE TERHADAP KEKUATAN IMPAK PADA PROSES BRAZING BAJA KARBON RENDAH EFFECT OF FLAME ON OXY-ACETYLENE WELDING ON IMPACT STRENGHT OF LOW CARBON STEEL BRAZING PROCESS PROYEK AKHIR Laporan akhir ini dibuat dan diajukan untuk memenuhi salah satu syarat kelulusan Sarjana Terapan Diploma IV Politeknik Manufaktur Negeri Bangka Belitung Disusun Oleh,” 2022.
M. A. Priadi, I. Nyoman, P. Nugraha, and G. Widayana, “THE EFFECT OF COOLING MEDIA TOWARD THE HARDNESS AND MICRO STRUCTURE THAT RESULT OXY ACETYLENE WELDING OF STEEL ST-37 MATERIAL,” 2017.
A. K. Rizqi, A. Hafizh, and A. Rasyid, “PENGARUH SUHU TEMPERING TERHADAP KETAHANAN BENDING DAN STUKTUR MIKRO SAMBUNGAN LAS SMAW BAJA SS400 SETELAH PROSES QUENCING DENGAN LARUTAN NaCl,” 2019.
N. Handra and P. I. Yudi, “STUDI KEKUATAN HASIL LAS OXY-ACETYLENE PADA VARIASI KAMPUH,” 2018.
A. Indraswara, “Reinterpreting Democracy Through Zizioulas’ Ontology of Personhood,” Jurnal Teologi, vol. 7, no. 2, pp. 105–122, Nov. 2018, doi: 10.24071/jt.v7i2.1199.
D. Jurusan Teknik Mesin Politeknik Negeri Ketapang Jurusan Teknik Mesin, P. Negeri Ketapang Jl Rangga Sentap, D. Pawan, and K. Barat, “PENGARUH PERLAKUAN TEMPERATUR PEMANASAN PADA HASIL PENGELASAN METODE SMAW TERHADAP HARDNESS LOGAM INDUK DAN LOGAM LAS,” Jurnal Sistem Teknik Industri, vol. 19, no. 1, 2017.
Downloads
Additional Files
Posted
License
Copyright (c) 2023 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.