Effect of Alkaline Potassium Hydroxide (Koh) On the Mechanical Strength of Sansivera Fiber Biocomposites
Pengaruh Alkali Kalium Hidroksida (Koh) Terhadap Kekuatan Mekanik Biokomposit Serat Sansivera
DOI:
https://doi.org/10.21070/ups.1404Keywords:
Potassium Hydroxide (KOH), Tensile Strength, Sansivera FiberAbstract
This study aims to analyze sansivera leaf fiber reinforced composite material with an alkaline concentration of 4% KOH along with a polyester resin matrix. Composite mixtures are divided into 6 types, namely Specimen 1 volume fraction 10%, Specimen 2 volume fraction 20%, Specimen 3 volume fraction 30%, Specimen 4 volume fraction 40%, Specimen 5 volume fraction 50%, Specimen 6 volume fraction 60%, Furthermore, for the composite tensile test process through the ASTM 638-03 method, which produces tensile strength data on the highest composite owned by Segment 2 with a value of 275 N / mm2 and the maximum load owned by Specimen 2 with a value of 42.30 N. The sansivera leaf fiber composite material and polyester resin matrix have mechanical properties, if the composite has a volume fraction with a very large value, the tensile strength on the specimen will be lower.
Downloads
References
Aisyah, W., Harijati, N., Arumingtyas, E.L., 2011. Kajian Morfologi, Anatomi dan Serat Daun Tanaman Sansevieria trifasciata yang Terdapat di Kota Malang. Diterima Tanggal 11 Sept. 2011 Direvisi Tanggal 6 Oktober 2011 NATURAL B, Vol. 1, No. 2, Oktober 2011, 121–122.
Aoladi, L.F., Pramono, C., Salahudin, X., 2019. Analisis Pengaruh Perlakuan Alkali Terhadap Kekuatan Tarik Dan Ketangguhan Impact Komposit Dari Serat Lidah Mertua ( Sansivera Trifasciata) Dengan Matrik Polyester.
Arif, Z., Adlie, T.A., Bahri, S., 2016. Analisa kekuatan mekanik material komposit polymeric foam diperkuat serat ampas tebu akibatT beban statik. 4.
Fahmi, H., Hermansyah, H., 2011. Pengaruh Orientasi Serat Pada Komposit Resin Polyester/ Serat Daun Nanas Terhadap kekuatan Tarik.
Hasyim, U.H., Yansah, N.A., Nuris, M.F., 2018. Modifikasi Sifat Kimia Serbuk Tempurung Kelapa (STK) Sebagai matriks Komposit Serat Alam Dengan Perbandingan Alkalisasi NAOH DAN KOH 1–7.
Lamalo, E.M.Y., 2017. Program Study Teknik Mesin Jurusan Teknik Mesin Fakultas Sains Dan Teknologi Universitas Sanata Dharma Yogyakarta.
Mardiyati, M., 2018. Komposit Polimer Sebagai Material Tahan Balistik. J. Inov. Pertahanan Dan Keamanan 1, 20–28. https://doi.org/10.5614/jipk.2018.1.1.3
Meiyasa, F., Tarigan, N., 2019. Peranan Kalium Hidroksida (KOH) Terhadap Mutu Karaginan Eucheuma cottonii di Indonesia. AGRISAINTIFIKA J. Ilmu-Ilmu Pertan. 2, 131. https://doi.org/10.32585/ags.v2i2.263
Nugraha, I.N.P., Dantes, K.R., Wigraha, N.A., 2017. Pemanfaatan limbah serat sebagai penguat untuk pembuatan material komposit bagi siswa smk se kabupaten buleleng.
Rizeki, C.A., Kastiawan, I.M., 2018. Analisa pengaruh orientasi arah serat terhadap kekuatan tarik dan impact kekuatan serat alam (Serat agave dan serat sansivera).
Sabuin, A., Boimau, K., Adoe, D. G. H., Mesin, J. T., & Cendana, U. N. "Pengaruh Temperatur Pengovenan Terhadap Sifat Mekanik Komposit HibridPolyester Berpenguat Serat Glass Dan Serat Daun Gewang lontar." 2015: 511(1),27-28
Gustiawan, Afandi. "Analisa Penggunaan Serat Daun Nanas Sebagai Bahan Alternatif Pembuatan Komposit Dengan Variasi Alkali KOH Ditinjau Dari Kekuatan Tarik." 2022.
Witono. "Pengaruh Perlakuan Alkali (NaOH) terhadap Kekuatan Tarik dan Morfologi Serat Mendong." 2013
.
Downloads
Additional Files
Posted
License
Copyright (c) 2023 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.