Analysis of The Effect of Preheating Temperature on the Tensile Strength Of Aluminium 5083 In A Vertical Position Using Shield Metal Arc Welding (SMAW)
Analisis Pengaruh Suhu Preheating Terhadap Kekuatan Tarik Aluminium 5083 pada Posisi Vertikal Menggunakan Shield Metal Arc Welding(SMAW)
DOI:
https://doi.org/10.21070/ups.1385Keywords:
Aluminium 5083, Preheating, SMAWAbstract
Aluminium 5083 an alloy of aluminium that has good cortical, power and welding resilience. Preheating on aluminium 5083 still possible in a particular temperature range. This research aimed to determine temperature preheating affected on aluminium 5083 vertical drag with SMAW. The various of preheating temperature was no preeating (spesimen 1), preheating at 40oC (spesimen 2) and preheating at 80 oC (spesimen 3). Based on test found that value of ultimate tensil strength on non preheating spesicimen was 301,894 MPa and experienced an increased 8,748% or 304,535 MPa on specimen with preheating at temperature 40oC, and on specimen with preheating at temperature 80oC value of ultimate tensil strength decline of 16,023% or 253,521 MPa.
Downloads
References
I. A. Kuntar, "Studi Eksperimental Friction Stir Welding Aluminium 5083 dengan Variasi Kecepatan Putaran dan Kemiringan Tool," Master's thesis, Institut Teknologi Sepuluh Nopember, Surabaya, 2016.
R. Harsono, S. M. Respati, and H. Purwanto, "Analisis Pengelasan SMAW Tegangan DC terhadap Kekuatan Tarik, Kekerasan, Foto Makro, dan Mikro pada Stainless Steel 304," Jurnal Momentum, vol. XV, pp. 58-63, 2019.
M. Darsin, S. Junusii, and Y. I. Triawan, "Analisa sifat mekanik dan struktur mikro paduan Aluminium 5083 akibat pengelasan metal inert gas (MIG) dengan variasi preheat dan post heat," Jurnal ROTOR, vol. 3, no. 2, pp. 67-74, 2010.
B. Bagus, S. M. Respati, and M. Dzulfikar, "Pengaruh Posisi Pengelasan Terhadap Kekuatan Tarik, Foto Makro dan Mikro pada Baja ST 37 dengan Pengelasan SMAW untuk Rangka Billboard," Jurnal Momentum, vol. XV, no. 2, pp. 132-136, 2019.
A. Rifaldi, A. U. Ryadin, and A. R. Hakim, "Pengaruh suhu Preheating Terhadap Kekuatan Tarik dan Kekerasan Pelat Baja ASTM A36 pada Pengelasan Shielded Metal Arc Welding (SMAW)," Jurnal Sigma Teknika, vol. IV, no. 1, pp. 81-90, 2021.
E. Gunawan, D. Perdana, and M. Subekti, "Analisa Pengaruh Variasi Tipe Sambungan Terhadap Sifat Mekanis pada Pembuatan Tangki BBM dari Bahan Aluminium Dilakukan Dua Welder Secara Bersamaan dengan Menggunakan Pengelasan GTAW," Jurnal Seniati, 2019.
D. Radaj, "Heat Effects of Welding," Berlin: Springer-Verlag, 1992.
R. C. Kusuma, S. Jokosisworo, and A. W. B. Santosa, "Analisis Perbandingan kekuatan tarik, impak, tekuk dan mikrografi aluminium 5083 Pasca pengelasan TIG (Tungsten Inert Gas) dengan Media pendingin air laut dan oli," Jurnal Teknik Perkapalan, vol. 5, no. 4, 2017.
Teng and Lin, "Effect of Welding Conditions on Residual Stresses due to Butt Welds," International Journal of Pressure Vessels and Piping, vol. LXXV, pp. 857-864, 1998.
N. Ahmadi, "Pengaruh Suhu Preheat dan Variasi Arus Pada Hasil Las Tig Aluminium Paduan terhadap Kekuatan Tarik dan Kekerasan," Jurnal Angkasa, vol. VIII, no. 1, pp. 159-166, 2016.
Sirama, "Pengaruh Preheat terhadap Laju Perambatan Retak Fatik Sambungan Las TIG pada Pengelasan Aluminium Paduan 6061-T6," 2014.
U. Prasmayobi, "Studi Kekuatan Bending Dan Kekerasan Pada Pengelasan Aluminium Dengan Menggunakan Las Smaw (Shielded Metal Arc Weling)," Skripsi, Jurusan Teknik Mesin Fakultas Teknik Universitas Halu Oleo, 2016.
P. Wibowo, "Analisis Pengaruh Preheat atau Pemanasan Awal Terhadap Hasil Pengelasan Ulang Aluminium 5083 Ditinjau dari Sifat Mekanik dan Metalurgi pada Lambung Kapal," Surabaya: Institut Teknologi Sepuluh Nopember, 2015.
S. N. Hidayat, "Pengaruh Suhu Preheat Terhadap Sifat Mekanis (Tarik, Kekerasan) dan Struktur Mikro Sambungan Butt Joint Dengan Pengelasan SMAW Pada Baja Karbon," Yogyakarta: Institut Teknologi Nasional Yogyakarta, 2016.
D. Y. Akbar, Wartono, and D. R. Hartana, "Pengaruh Temperatur Preheat terhadap Sifat Mekanis Las SMAW pada Baja Karbon," Jurnal Cendekia Mekanika, vol. I, no. 1, pp. 47-56, 2020.
Downloads
Additional Files
Posted
License
Copyright (c) 2023 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.