Impact Strength and Hardness Analysis of Sansevieria Fiber Composites with Variations in Starch Addition
Analisis Kekuatan Impact Dan Kekerasan Komposit Serat Sansevieria Dengan Variasi Penambahan Amilum
DOI:
https://doi.org/10.21070/ups.9452Keywords:
Natural Fibe, Sansevieria Fiber, AmylumAbstract
Natural fibers are abundant in nature and are often underutilized. This research aims to utilize fiber addition and amylum variation on impact strength and hardness of composites. The composite material used consists of Sansevieria fiber and amylum as reinforcement and polyester resin. This research was conducted using amylum variations of 0%, 6%, 7%, 8%, 9%, 10% and fibers cut with a length range of 0.5 cm. The composite manufacturing process uses the hand-lay-up method. Composite testing uses ASTM 5942-96 standard for impact test and ASTM-2440 standard for hardness test. The highest hardness test results were achieved by composites with 9 and 10% amylum composition with a value of 80.3 Shore D. The highest Impact Effort (E) achieved by the composite with 6% amylum variation is 4.026 Joule, the highest Impact Price achieved by the composite with 6% amylum variation is 0.2013 〖Joule/mm〗^2.
Downloads
References
M. Muhajir, M. A. Mizar, D. A. Sudjimat, and J. P. T. Mesin-ft, “ANALISIS KEKUATAN TARIK BAHAN KOMPOSIT MATRIKS RESIN BERPENGUAT SERAT ALAM DENGAN BERBAGAI VARIAN TATA LETAK,” J. Tek. MESIN, no. 2, pp. 1–8, 2016.
A. Latifa, “Pengaruh Variasi Tebal Core Dan Fraksi olume Terhadap Kekuatan Mekanik Komposit Sandwich Polyester Berpenguat Serat Daun Nanas Dengan Core Styrofoam,” 2015. [Online]. Available: http://repository.unej.ac.id/bitstream/handle/123456789/65672/Ainul Latifah-101810401034.pdf?sequence=1
A. Muhni, “Pemanfaatan Serat Buah Pinang Sebagai Penguat Susunan Acak ( Random ) Dan Resin Poliester Sebagai Matriks pada Material Biokomposit,” p. 73, 2021.
R. Wanti, H. Dzulfikar, and R. Rudy, “Ekstraksi dan Karakterisasi Serat Alam dari Daun Sansevieria Laurenti dan Sansevieria Zeylinic,” vol. 18, no. 2, pp. 88–104, 2020, doi: 10.53298/texere.v18i2.59.
S. S. Kelana, “Pengaruh Perbandingan Fraksi Volume Serat Aren dan Serat Daun Nanas pada Pembuatan Material Komposit,” Din. J. Ilm. Tek. Mesin, vol. 13, no. 1, p. 1, 2021, doi: 10.33772/djitm.v13i1.18683.
A. Delni Sriwita, “PEMBUATAN DAN KARAKTERISASI SIFAT MEKANIK BAHAN KOMPOSIT SERAT DAUN NENAS- POLYESTER DITINJAU DARI FRAKSI MASSA DAN ORIENTASI SERAT,” J. Fis. Unand, vol. 3, no. 1, pp. 30–36, 2014, [Online]. Available: ISSN 2302-8491
P. H. Tjahjanti, Buku Ajar Teori Dan Aplikasi Material Komposit Dan Polimer. Sidoarjo: UMSIDA Press, 2018. doi: 10.21070/2019/978-602-5914-27-0.
H. Fena Retyo Titani, Calaelma Logys Imalia, “Pemanfaatan Serat Sabut Kelapa Sebagai Material Penguat Pengganti Fiberglass Pada Komposit Resin Polyester Untuk Aplikasi Bahan Konstruksi Pesawat Terbang,” vol. 19, no. 1, pp. 23–28, 2018.
E. Widodo, Buku Ajar Mekanika Komposit dan Bio-Komposit. Sidoarjo: UMSIDA Press, 2022.
M. Y. Ali, “Analisis Kekuatan Uji Impak Komposit Serat Alam ( Serat Batang Pisang ),” Anal. Kekuatan Uji Impak Komposit Serat Alam ( Serat Batang Pisang ), vol. 23, no. 1, pp. 35–38, 2022.
A. Firdaus, “Analisis pengaruh bentuk filler pada komposit batang bambu terhadap nilai kekerasan (hardness shore d),” 2017.
A. Asroni and S. Dri Handono, “Kaji Eksperimen Variasi Jenis Serat Batang Pisang Untuk Bahan Komposit Terhadap Kekuatan Mekanik,” Turbo J. Progr. Stud. Tek. Mesin, vol. 7, no. 2, pp. 214–222, 2018, doi: 10.24127/trb.v7i2.764.
P. R. Sari, B. D. Pambudi, R. St., and A. W. Ningrum, “Prosiding Seminar Nasional Kesehatan 2021 Lembaga Penelitian dan Pengabdian Masyarakat heterophyllus L .) dengan Menggunakan Metode Prosiding Seminar Nasional Kesehatan 2021 Lembaga Penelitian dan Pengabdian Masyarakat,” Karakterisasi Sifat Fis. Granul Dengan Bahan Pengikat Amylum Manihot Pragelatinasi Dan Polivinilpirolidon Rela, no. Program Studi Sarjana Farmasi, Fakultas Ilmu Kesehatan, Universitas Muhammadiyah Pekajangan Pekalongan, pp. 1182–1193, 2021.
E. Widodo, P. H. Tjahjanti, and F. S. Kirom, “The sansevieria trifasciata fiber compatibility analysis for biocomposite reinforcement Analisis kompatibilitas serat sansevieria trifasciata untuk penguat biocomposite,” vol. 10, no. 1, pp. 99–103, 2021
Downloads
Additional Files
Posted
License
Copyright (c) 2025 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.