The Effect of Sansevieria Fiber Orientation Variation on Tensile and Bending Mechanical Strength in Composite
Pengaruh Variasi Orientasi Serat Sansevieria terhadap Kekuatan Mekanik Tarik dan Bending dalam Pembuatan Komposit
DOI:
https://doi.org/10.21070/ups.8153Keywords:
Leave Sansevieria, Fiber Orientation, Natural FiberAbstract
The snake plant or sansevieria is known as one of the plants that are easily found in Indonesia. This study aims to determine the effect of variations in the orientation of straight, zigzag and perpendicular fibers on the mechanical tensile and bending strength of composites using ASTM D638 for tensile testing and ASTM D790 for bending testing. In the tensile test, the largest stress was found in the straight orientation variation with a value of 23.17 N/, the largest strain was found in the perpendicular orientation variation with a value of 0.1596 N/ and the largest modulus of elasticity was found in the straight orientation variation with a value of 216.01 Mpa. Meanwhile, in the bending test, the largest stress was found in the straight fiber orientation variation with a value of 71 N/and the largest elastic modulus was found in the straight fiber orientation variation value of 12128 Mpa.
Downloads
References
M. Syaukani, F. Paundra, F. Qalbina, I. Dwi Arirohman, P. Yunesti, dan Sabar, “Desain dan Analisis Mesin Press Komposit Kapasitas 20 Ton,” J. Sci. Technol. Soc. Cult. , vol. 1, no. 1, hal. 29–34, 2021.
E. Widodo dan T. T. Kurniawan, “Experimental Study on Sansivera Composite Fibers Against the Administration of Alkaline NaOH (Sodium Hydroxide),” Procedia Eng. Life Sci., vol. 4, no. June, hal. 7–13, 2023, doi: 10.21070/pels.v4i0.1411.
R. Manurung, S. Simanjuntak, J. Sembiring, R. A. M. Napitupulu, dan S. Sihombing, “Analisa Kekuatan Bahan Komposit Yang Diperkuat Serat Bambu Menggunakan Resin Polyester Dengan Memvariasikan Susunan Serat Secara Acak Dan Lurus Memanjang,” Sprocket J. Mech. Eng., vol. 2, no. 1, hal. 28–35, 2020, doi: 10.36655/sproket.v2i1.296.
N. A. Kurniawan, F. Setiawan, dan E. Sofyan, “Pengujian Tarik Komposit Spesimen Campuran Serat Pisang Alur Diagonal Dan Pasir Besi Dengan Matrik Resin Polyester Dengan Metode Hand Lay-Up,” Tek. STTKD J. Tek. Elektron. Engine, vol. 8, no. 2, hal. 281–288, 2022, doi: 10.56521/teknika.v8i2.657.
H. I. Firmansyah, W. Wirawan, dan M. N. Hariyanto, “Analysis of Fiber Metal Composite Shear Strength Using Independent Variables of Fiber Angle Orientation and Metal Surface Roughness,” J. Energi dan Teknol. Manufaktur, vol. 5, no. 02, hal. 29–34, 2022, doi: 10.33795/jetm.v5i02.136.
I. A. Kusumaningtyas dan U. Wahyuningsih, “Analisa Hasil Penelitian Tentang Teknik Ecoprint Menggunakan Mordan Tawas, Kapur, dan Tunjung Pada Serat Alam,” J. Scr., vol. 10, no. 3, hal. 9–14, 2021.
D. Ginting, R. F. Syahputra, dan W. Jannah, “Biokomposit Papan Partikel diperkuat Serat Alam Sabut Kelapa dan Tempurung Kelapa dan matriks epoksi,” JMPM (Jurnal Mater. dan Proses Manufaktur), vol. 7, no. 1, hal. 53–62, 2023, doi: 10.18196/jmpm.v7i1.18375.
T. Widowati dan Fatchuroh, “Kelayakan Serat Lidah Mertua ( Sansevieria Trifasciata ) Sebagai Bahan Pembuatan Bulu Mata Palsu untuk Rias,” J. Scr. unnes, vol. 10, no. 1, hal. 26–29, 2021.
Mulyadi, E. Widodo, P. H. Tjahjanti, dan F. S. Kirom, “The sansevieria trifasciata fiber compatibility analysis for biocomposite reinforcement,” Turbo J. Progr. Stud. Tek. Mesin, vol. 10, no. 1, hal. 99–103, 2021, doi: 10.24127/trb.v10i1.1542.
P. H. Tjahjanti, E. Widodo, dan Mulyadi, “Characterization of Sansevieria Fiber with NaOH Alkalization to Increase Tensile Strength,” IOP Conf. Ser. Earth Environ. Sci., vol. 1104, no. 1, 2022, doi: 10.1088/1755-1315/1104/1/012030.
V. T. Putri, A. Pramita, dan T. E. P. Sri Rahayu, “Sintesis Selulosa Asetat dari Tanaman Lidah Mertua (Sansevieria trifasciata) sebagai Membran Pereduksi CO (Karbon Monoksida) pada Asap Rokok,” J. Rekayasa Hijau, vol. 5, no. 3, hal. 281–290, 2022, doi: 10.26760/jrh.v5i3.281-290.
E. W. Febriyanto dan E. Widodo, “Analysis Of Sansevieria Fiber Composite With Naoh Alkalization Analisa Komposit Serat Lidah Mertua (Sansevieria) Dengan Perlakuan Alkali Naoh,” vol. 0672, no. c, hal. 959–966, 2022, [Daring]. Tersedia pada: https://pssh.umsida.ac.id.
T. T. Kurniawan dan E. Widodo, “Experimental Study on Sansivera Composite Fibers Against the Administration of Alkaline NaOH (Sodium Hydroxide),” Procedia Eng. Life Sci., vol. 4, no. June, hal. 7–13, 2023, doi: 10.21070/pels.v4i0.1411.
H. Suryanto, “Karakterisasi fisik , kimia , ketahanan panas dan kekuatan tarik dari Serat Mendong ( Fimbristylis globulosa ),” Jur. Tek. Mesin Univesitas Negeri Malang, no. January, hal. 1–12, 2017.
A. Fa’iz, F. Setiawan, dan E. Sofyan, “Pengujian Karakteristik Uji Impact Material Komposit Matriks Resin Polyester Campur Serat Pisang Dan Pasir Besi Dengan Variasi Berat,” Tek. STTKD J. Tek. Elektron. Engine, vol. 8, no. 2, hal. 274–280, 2022, doi: 10.56521/teknika.v8i2.656.
C. Gautama R, M. F. Alfatih, dan S. Alimi, “Eksperimen Uji Bending Pada Komposit Resin Polyester Dan,” J. Tek. Elektron. Engine Engine, vol. 8, no. 2, hal. 237–242, 2022.
V. Viani dan U. Prayudie, “Pengaruh Penambahan Serat Biduri (Calotropis Gigantea) Terhadap Sifat Mekanik Komposit Polipropilena Daur Ulang/Serat Biduri,” J. Polym. Chem. Eng. Technol., vol. 1, no. 1, hal. 17–22, 2024, doi: 10.52330/jpcet.v1i1.237.
U. F. Hamid dan Wijianto, “Effek Perlakuan Alkali Natrium Hiroksida Terhadap Karakter Fisis dan Mekanis Komposit Serat Nanas Dengan Penguat Resin Poliester,” Nucl. Phys., vol. 13, no. 1, hal. 104–116, 2023.
M. Rusly, R. Sulistyowati, dan P. Lumban Toruan, “Analisis Uji Tarik Komposit Serat Batang Kelakai Dengan Variasi Katalis Untuk Pembuatan Material Bumper Mobil,” J. Online Phys., vol. 9, no. 1, hal. 43–44, 2023, doi: 10.22437/jop.v9i1.27670.
E. Widodo dan W. Nugroho, “Studi kekuatan kekerasan dan kekuatan impact pada komposit diperkuat serat sansevieria dengan variasi penambahan amilum 6 % -10 %,” vol. 20, no. 1, hal. 164–174, 2025.
M. Arsyad dan K. Yan, “Efek Perlakuan Natrium Hidroksida Terhadap Kekuatan Tarik Komposit Serabut Kelapa,” komposit, hal. 16–21, 2020.
B. S. Wicaksono, “Pengaruh Variasi Lama Prendaman Serat Tebu Dengan NaOH Terhaadap Kekuatan Bending Dan Struktur Mikro Pada Komposit Matriks Polyester BQTN 157-EX,” PENGARUH VARIASI LAMA PERENDAMAN SERAT TEBU DENGAN NAOH TERHADAP KEKUATAN Bend. DAN Strukt. MIKRO PADA KOMPOSIT MATRIKS Polyest. BQTN 157-EX., vol. 09, no. 03, hal. 123–128, 2021.
ASTM D638, “Standard Test Method for Tensile Properties of Plastics,” ASTM Stand., vol. 08, hal. 1–16, 2014, doi: 10.1520/D0638-14.1.
A. D790, “iTeh Standards iTeh Standards Document Preview,” vol. 08, no. Reapproved 1989, hal. 3–4, 2000, doi: 10.1520/C1709-18.
S. A. Rahmawaty, “Analisa Kekuatan Tarik dan Tekuk pada Komposit Fiberglas-Polyester Berpenguat Serat Gelas dengan Variasi Fraksi Volume Serat,” JTM-ITI (Jurnal Tek. Mesin ITI), vol. 5, no. 3, hal. 146, 2021, doi: 10.31543/jtm.v5i3.685.
P. N. Kirana, “Sifat mekanik komposit bermatriks polimer dengan penguat serat panjang daun Sansevieria Trifasciata,” J. Itenas, hal. 1–11, 2021.
R. Ruzuqi dan V. D. Waas, “Analisis Kekuatan Tarik Dan Impak Material Komposit Polimer Dalam Aplikasi Fiberboat,” ALE Proceeding, vol. 4, hal. 121–126, 2021, doi: 10.30598/ale.4.2021.121-126.
D. I. Sakti et al., “Studi Perbandingan Investigasi Modulus Elastisitas Antara Metode Uji Tarik dengan Metode Indentasi Pada Material Styrene BUTADIENE RUBBER 25 (SBR-25),” J. Tek. Mesin S-1, vol. 11, no. 2, hal. 147–156, 2023.
F. M. Fais, “Rancang Bangun Alat Uji Bending Sistem Hidrolik,” hal. 47–53, 2022.
C. A. Siagian, D. Wicaksono, dan F. Setiawan, “Analisis Uji Tarik Dan Uji Bending Dengan Karakteristik Honeycomb Polylactic Acid (Pla) Terhadap Variasi Suhu Ruangan,” Tek. STTKD J. Tek. Elektron. Engine, vol. 9, no. 2, hal. 256–261, 2023, doi: 10.56521/teknika.v9i2.940.
H. Setiawan, T. C. Wahyudi, dan M. Thohirin, “Analisa variasi arus listrik pada proses pengelasan Shielded Metal Arc Welding (SMAW) baja karbon sedang terhadap kekuatan bending hasil pengelasan,” ARMATUR Artik. Tek. Mesin Manufaktur, vol. 3, no. 2, hal. 88–97, 2022, doi: 10.24127/armatur.v3i2.2864.
Downloads
Additional Files
Posted
License
Copyright (c) 2025 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.