Impact Strength and Hardness Study of Kenaf Fiber Reinforced Composites with Variations in Starch Concentration
Studi Kekuatan Impak dan Kekerasan Pada Komposit Diperkuat Serat Kenaf dengan Variasi Konsentrasi Penambahan Amilum
DOI:
https://doi.org/10.21070/ups.11099Keywords:
composite, kenaf fiber, AmilumAbstract
This study aims to analyze the effect of variations in the addition of Manihot esculenta starch on the impact strength and hardness of kenaf fiber-reinforced polymer composites. The composite material was made using a polyester resin matrix with kenaf fiber reinforcement that had been treated with alkali using 5% NaOH solution for 2 hours. Variations in starch addition were carried out at 0%, 1%, 2%, 3%, 4%, and 5%. Impact testing was carried out using the Charpy method based on ASTM D5942-96, while hardness testing used Shore D based on ASTM D2240. The results showed that increasing starch concentration caused a decrease in the impact value of the composite. The highest absorption energy value was obtained in the specimen without starch addition of 5.402 Joules, while the lowest value was found in the 5% starch variation of 3.900 Joules.
Downloads
References
S. Hariyadi And B. Junipitoyo, “Pelatihan Basic Wet Lay Up Composite Repair System Untuk Sekolah Vokasi Penerbangan,” Vol. 01, No. 02, Pp. 64–72, 2021.
T. H. Ningsih, A. Fiveriati, And F. W. Irfani, “Kekuatan Dan Momen Bending Serta Energi Impak Komposit Serat Kulit Kersen Akibat Variasi Fraksi Volume,” J. Inov. Teknol. Manufaktur, Energi, Dan Otomotif, Vol. 1, No. 2, Pp. 95–104, 2023, [Online]. Available: Http:Https://Jurnal.Poliwangi.Ac.Id/Index.Php/Jinggo/
Nadya Ophelia, I.B Putra Jandhana, Jupriyanto, And George Royke Deksino, “Eksplorasi Penggunaan Bahan Material Komposit Dari Serat Alam Pada Drone: Jurnal Review,” J-Proteksion J. Kaji. Ilm. Dan Teknol. Tek. Mesin, Vol. 9, No. 1, Pp. 46–55, 2024, Doi: 10.32528/Jp.V9i1.2033.
E. Widodo Et Al., “Studi Kekuatan Kekerasan Dan Kekuatan Impact Pada Komposit Diperkuat Serat Sansevieria Dengan Variasi Penambahan Amilum 6 % -10 %,” Vol. 20, No. 1, Pp. 164–174, 2025.
T. H. R. Side, R. Mastuti, And A. R. Widiani, “Efektivitas Teknik Skarifikasi Untuk Mematahkan Dormansi Benih Kenaf (Hibiscus Cannabinus L.),” J. Littri, Vol. 27, No. 1, Pp. 34–3, 2021, [Online]. Available: Http://Dx.Doi.Org/10.21082/Littri.
A. M. K. Nisa And A. F. Rizki, “Optimasi Metode Degumming Pada Serat Daun Nipah Menggunakan Enzim Pektinase Dan Natrium Bikarbonat,” Pp. 1–73, 2023.
R. Wanti, H. Dzulfikar, And R. Rudy, “Ekstraksi Dan Karakterisasi Serat Alam Dari Daun Sansevieria Laurenti Dan Sansevieria Zeylinic,” Texere, Vol. 18, No. 2, Pp. 88–104, 2020, Doi: 10.53298/Texere.V18i2.59.
E. Widodo, Buku Ajar Mekanika Komposit Dan Bio-Komposit Penulis.
E. Widodo, Pratikto, Sugiarto, And T. D. Widodo, “Comprehensive Investigation Of Raw And Naoh Alkalized Sansevieria Fiber For Enhancing Composite Reinforcement,” Case Stud. Chem. Environ. Eng., Vol. 9, No. August 2023, P. 100546, 2024, Doi: 10.1016/J.Cscee.2023.100546.
A. Abdirullah And M. Bayu Prakoso, “Implementasi Analisis Karakteristik Komposit Serat Knaf Menggunakan Metode Uji Impak Untuk Beberapa Jenis Rincian Ukuran Kecil Implementation Of Knaf Fiber Composite Characteristics Analysis Using The Impact Test Method For Several Types Of Small Size Det,” Jmemme, Vol. 4, No. 2, Pp. 94–101, 2020, [Online]. Available: Http://Ojs.Uma.Ac.Id/Index.Php/Jmemme
T. Manurung, “Analisis Perbandingan Kekuatan Bahan Komposit Dengan Variasi Susunan Acak Dan Lurus Memanjang Berbasis Serat Bambu Dan Resin Polyester,” J. Kolaborasi Sains Dan Ilmu Terap., Vol. 1, No. 1, Pp. 19–23, 2022, Doi: 10.69688/Juksit.V1i1.5.
K. Boimau, “Efek Temperatur Terhadap Sifat Tarik Komposit Poliester Berpenguat Serat Daun Gewang,” Jmpm (Jurnal Mater. Dan Proses Manufaktur), Vol. 6, No. 1, Pp. 11–18, 2022, Doi: 10.18196/Jmpm.V6i1.14806.
S. Pangan, R. Aristyarini, And S. Yasni, “Peningkatan Serat Pangan Larut Dari Ampas Tahu Dan Sifat Fungsionalnya Dengan Perlakuan Fisik: Tinjauan Literatur,” J. Teknol. Ind. Pertan., Vol. 32, No. 1, Pp. 84–95, 2022, Doi: 10.24961/J.Tek.Ind.Pert.2022.32.1.84.
J. T. Mesin, F. T. Industri, And U. I. Indonesia, “Pembuatan Produk Komposit Hand Guard Sepeda Motor Touring Berpenguat Woven Carbon Fiber Menggunakan Metode Compression Molding,” 2025.
A. Wahyu And M. Mutawally, “Rancang Bangun Alat Uji Impak Charpy Untuk Material Komposit Sebagai Media Pembelajaran Di Laboratorium Mekanik,” 2021.
J. Fery And W. Siadari, “Otomatis Dengan Maksimum Energi Impak 300 Joule Skripsi Oleh : Fakultas Teknik Universitas Medan Area Medan Otomatis Dengan Maksimum Energi Impak 300 Joule Skripsi Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Sarjana Di Fakultas Teknik Univer,” 2023.
I. P. Putra, “Analisa Uji Tarik Dan Impak Penguat Karbon, Campuran Epoxy-Karet Silikon 30%,40%,50%, Rami, Dan Kapas Matrik Epoxy,” Itenas Malang, Pp. 4–31, 2020.
K. K. Nikel, “Sifat Tarik , Kekerasan , Dan Kemagnetan,” 2025.
A. C. Ararya And D. Oktavia, “J-Teta : Jurnal Teknik Terapan,” Vol. 3, No. 2, Pp. 2–7, 2024.
M. L. S. Fikri Et Al., “Pengaruh Variasi Fraksi Massa Bio-Fiber Dengan Perlakuan,” Vol. 8, No. 3, Pp. 146–153, 2025.
U. M. Area, “Pembuatan Mesin Uji Impak Charpy Semi Otomatis Dengan Maksimum Energi Impak 300 Joule Skripsi Oleh : Albet Juanda Purba Fakultas Teknik Universitas Medan Area Medan Otomatis Dengan Maksimum Energi Impak 300 Joule Skripsi Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Sarjana Di Fakultas Teknik Universitas Medan Area Oleh : Albert Juanda Purba Fakultas Teknik Medan,” 2024.
S. F. Materials, “Jeee : Journal Of Educational Engineering And Environment,” Vol. 4, No. April, Pp. 20–26, 2025.
D. Sebagai, S. Memperoleh, G. Sarjana, P. Studi, T. Material, And U. Malikussaleh, “Pemanfaatan Limbah Hdpe Sebagai Matrik Pada Komposit Diperkuat Serat Ijuk Untuk Produk Otomotif Disusun Sebagai Syarat Memperoleh Gelar Sarjana Teknik Program Studi Teknik Material Universitas Malikussaleh,” 2024.
R. Arjmandi Et Al., “Kenaf Fibers Reinforced Unsaturated Polyester Composites : A Review,” 2021, Doi: 10.1177/15589250211040184.
P. Komposisi, S. Kenaf, D. A. N. Serbuk, A. H. Laksana, And M. B. Waluyo, “Terhadap Kekuatan Tekuk Dan Water Absorption Komposit Hybrid -Poliester,” Vol. 1, No. 2, 2021.
A. Sivasamy, H. Soo, J. Kim, S. Lee, And T. June, “Nanostructured Fe 2 O 3 @ Nitrogen-Doped Multiwalled Nanotube / Cellulose Nanocrystal Composite Material Electrodes For High-Performance Supercapacitor Applications,” Integr. Med. Res., Vol. 9, No. 4, Pp. 7615–7627, 2020, Doi: 10.1016/J.Jmrt.2020.05.058.
A. N. Aina Et Al., “Fiber ‑ Reinforced Thermoplastic Composites For Future Use In Aircraft Radomes : Biomimetic Design Approaches And Its Performances,” Fibers Polym., Vol. 25, No. 12, Pp. 4503–4527, 2024, Doi: 10.1007/S12221-024-00776-1.
N. Parthipan, S. Gowsik, S. N. Kumar, And M. P. Kumar, “Investigation Of Hardness And Impact Test In Silane Treated Silicon Added Kenaf Hybrid Composite Material,” Vol. 12, No. 11, Pp. 5592–5598, 2021.
O. V Arzhakova, A. A. Dolgova, A. Y. Yarysheva, And A. A. Zezin, “Controlled Green Synthesis Of Hybrid Organo-Inorganic Nanomaterials Based On Poly ( Ethylene Terephthalate ) And Silver Nanoparticles By X-Ray Radiolysis,” Vol. 15, No. 6, Pp. 531–540, 2021.
B. B. Dasar, “Review : Produksi Plastik Biodegradable Berbahan Dasar Tongkol Jagung Sebagai Bahan Kemasan,” Vol. 11, No. 1, Pp. 177–194, 2025.
P. Lanyo, G. S. Lubis, And M. Ivanto, “Analisis Pengaruh Perlakuan Panas Terhadap Perubahan Nilai Kekerasan Baja Karbon Aisi 1045,” Vol. 6, No. 2, Pp. 63–70, 2025.
K. Agama, L. Penelitian, D. A. N. Pengabdian, U. Islam, N. Maulana, And M. Ibrahim, “Studi Pengaruh Variasi Fraksi Volume Filler Partikel Cangkang Kerang Hijau,” 2021.
V. N. Juli Et Al., “Karakterisasi Sifat Mekanik Dan Mikrostruktur Komposit Berbasis Serat Kulit Lantung Dan Eceng Gondok Menggunakan Resin Polyester Lingkungan Karena Penyebarannya Yang Tak Terkendali . Namun , Batang Eceng Gondok,” Vol. 1, Pp. 67–81, 2022, Doi: 10.63891/Impak.V1i2.70.
Downloads
Additional Files
Posted
Categories
License
Copyright (c) 2026 UMSIDA Preprints Server
This work is licensed under a Creative Commons Attribution 4.0 International License.